AMS 4928 Ti6Al4V Bar And Wire
Hot finished with or without subsequent cold reduction, annealed, and descaled. Unless prohibited by the purchaser, bars may be solution heat-treated before annealing. A machined or ground surface is permitted unless prohibited by the purchaser.
Alloy shall be multiple melted. The product shall be processed to the final thickness/diameter by metallurgical working operations prior to any straightening, dimensional sizing or surface finishing operations. Bar shall not cut from plate.
Cold drawn, annealed, and descaled.
Heat Treatment
Bars, wire, forgings, and flash welded rings shall be heat treated as follows; pyrometry shall be in accordance with AMS2750.
Solution Heat Treatment
When solution heat treatment is used, heat to a temperature within the range 50 to 150 °F (28 to 83 °C) degrees below the beta transit, hold at the selected temperature within ±25 °F (±14 °C) for a time commensurate with section thickness and the heating equipment and procedure used, and cool at a rate equivalent to an air cool or faster.
Annealing
Heat to a temperature within the range 1300 to 1450 °F (704 to 788 °C), hold at the selected temperature within ±25 °F (±14 °C) for not less than 1 hour, and cool as required.
Properties
The product shall conform to the following requirements and shall also meet the requirements of 3.5.1.1 after being heated to any temperature up to 1250 °F (677 °C), held at heat for 20 minutes ± 3, cooled in air, and descaled:
Bars, Wire, Forgings, and Flash Welded Rings
Product, 6 inches (152 mm) and under in nominal diameter or least distance between parallel sides, shall have the following properties:
Tensile Properties
Hot Tags: ams 4928 ti6al4v bar and wire, China ams 4928 ti6al4v bar and wire manufacturers, suppliers, factory, titanium, titanium rod for architecture industry, titanium rod benefits, titanium rod applications, titanium rod for thanksgiving decoration, north american titanium rod, Titanium Hollow Bar